Papers - Equilibrium Relations in Aluminum-magnesium Silicide Alloys Containing Excess Magnesium

Aluminum alloys containing magnesium and silicon are susceptible to strengthening and hardening by suitable heat-treatments, and they constitute a class of alloys of considerable commercial importance. Generally, they contain these two elements in the proportions required for the formation of the intermetallic compound Mg2Si, or an excess of silicon; no commercial wrought alloys are made with an appreciable excess of magnesium. The reason for not having excess magnesium is obvious from the results given in this paper, since it is shown that excess magnesium results in a proportional decrease in the solubility of Mg2Si. This is the eighteenthl of a series of papers from the Aluminum Research Laboratories dealing with the equilibrium relations in aluminum-alloy systems; most of the previous publications concerned binary aluminum-alloy systems; this is the fourth of a group pertaining to ternary aluminum-alloy systems. The work on this system was completed in 1930, but the results were not published because of the pressure of other work. Hanson and Gaylor2, in 1921, presented the results of an extensive investigation of the aluminum-magnesium-silicon system. Their results indicated that an excess of magnesium over the amount required to form the compound MgzSi caused a noticeable decrease in the solid solubility of MgzSi in aluminum. A more recent investigation3 in these laboratories showed that the solid solubility of MgzSi in aluminum was 1.85 per cent at 595' C. and decreased to 0.30 per cent at 300' C. The results of the latter investigation were used as the basis for the present work. The Present Investigation In the present investigation, a study was made of the effect of various amounts of excess magnesium upon the solid solubility of MgzSi in