Papers - New York Meeting – February, 1929 - Gases in a Sample of Overpoled Fire-refined Copper (With Discussion)

The writer has dealt with the effect of various methods of melting copper upon the gas content of the metal.' The copper referred to in his earlier paper was melted in the foundry both in the oil furnace and the electric furnace. As the metal did not measure up to conductivity standard, the term "casting copper" was applied to the material in the title of the paper. It was thought that some information in regard to the gases in a sample of overpoled copper might also be of interest, and through the courtesy of C. R. Stevens, superintendent of the copper mill of the West-inghouse Elec. & Mfg. Co., such a sample was obtained. The metal was chill-cast in the form of an ingot about 7 in. long, 2 1/2 in. deep (from the base to the raised surface of the ingot) and from 1 3/8 to 1 7/8 in. wide. A photograph of part of the ingot is shown in Fig. 1. The effect of over-poling on the surface of the metal is here quite clearly shown.