Papers - Plastic Deformation and Recrystallization of Aluminum Single Crystals

The process of plastic extension of face-centered cubic single crystalline rods is so well understood, since the notable studies of Taylor and Elam,1 that the change in orientation of any crystal by slip and rotation may be predicted from the measured elongation. It is customary to assume a very homogeneous deformation, wherein gliding lamellar arc free to rotate so that their slip direction continually approaches the axis of the rod, until a second slip system comes into operation; whereupon conjugate slip proceeds quantitatively to an end adjustment with the [121] direction in the axis of the rod. This process has been checked in malty face.-centered cubie materialsand and readily permits the preparation of specimens that have been subjtvted to various determinable amounts of shearing action. It is elearly of interest to study in such measurably strained speeimens the, development of a recrystallized structure on annealing and if possilble detect the source of nuclei from which the new crystals grow. Strain-:~nneali~ig experiments of this charactcr have been performed by others but not in detail sufficient to permit a study, for example, of the number of recrystallized grains vs. the amount of shear. In the experiments now reported, this was done with a wide variety of orientations covering nearly the entire range of slip on a single system and corresponding to amounts of shear (ratio of shearing distance to distance between lamellae at the conclusion of a test of from 0.08 to 0.57. A particular point wa-made of determining the crystallite rotation, or small angular range. assumed by the octahedral slip plane after these various amounts of shear. The, mechanism of reerystallization and the magnitude and effeet of recovery on the recrystallization process was investigated.