Papers - Sintering Limonitic Iron Ores at Ironton, Minnesota (With Discussion)

The first autlientic description of an iron bath for the deposition of iron is probably that of Bottger in 1846, who used a bath containing ferrous sulfate and ammonium chloride. In 1861, Kramer deposited iron from ferrous chloride solution. Electrolytic iron was produced in 1869 by Bietz, who used it for making some magnetic tests. In the same year, Klein is. said to have worked out his process. Jacobil in 1869 described the results obtained in electroplating with iron on copper for making dies and plates for bank notes, by Klein's process. A letter from Klein to Jacobi describes the bath more fully. It consisted of FeS04 + (NH4)2SO4. Lenz2 described some properties of electrolytically precipitated iron. He used Klein's bath, FeS0, + MgSO4 + MgCO3, to neutralize and obtained fine-grained and hard iron. His conclusions were as follows: 1. Electrolytic iron and copper contain gases, notably hydrogen. 2. The volume of gas absorbed by iron varies within wide limits, but it is easy for iron to take up very considerable quantities of gas. 3. The absorption of gas is principally in the first formed layers of iron. 4. When iron is heated, gas begins to come off below 100°, principally hydrogen. 5. Heated to redness, reduced iron oxidizes in water, in part at least at the expense of the oxygen of the water, decomposing it and setting free hydrogen, which is partly or wholly absorbed. Siemens,3 in 1889, was the first to propose a general process embodying a step for leaching a sulfide mineral with ferric chloride or sulfate and a step for regenerating the leach and depositing iron on a cathode in a diaphragm cell. So far as is known, Siemens did not carry out his patent