Papers - X-ray Investigations - X-ray Notes on the Iron-molybdemun and Iron-tungsten Systems (With Discussion)

In 1926 one of the authors published researches on the determination and description of the iron-tungsten and iron-molybdenum systems,' including the equilibrium diagrams. In 1929, further work was carried on, including the examination by X-rays, which is recorded here. Meas-urements were made of changes in lattice parameters in the solid solutions. Precipitation from the solid solution and the accompanying changes in hardness were studied as well as the formation of the intermetallic com-pound phases upon sintering a mixture of metal powders. Materials All the specimens were prepared from the same quality of metals and by the same methods as were described in the determination of the constitutional diagrams. The metal powders as mixed and pressed were sintered or fused in a hydrogen atmosphere and subsequently treated as indicated in the titles of the figures. The formation of the iron-rich solutlon in the solid was accomplished by sintering in hydrogen for a period of 20 to 30 hr. at a temperature 25' to 50' C. below the melting point of the eutectic. The tungsten-rich and molybdenum-rich solid solutions of iron were prepared by adding the iron as a solution of iron ammonium oxalate to the oxide of tungsten or molybdenum, followed by a hydrogen reduction. This method results in a homogeneous alloy after sintering the pressed metal powder for 20 to 30 hr. at a temperature slightly below that of the peritectic reaction in the system involved. For X-ray examination the specimens were variously prepared, depending on the nature of the sample and what it was desired to show. For example, the iron containing tungsten or molybdenum in solid solution was cut with a file, the chips were put through bolting cloth, and this powder of filings formed the specimens for comparative study. The