Part II - Communication - The Preparation of Thin Foils of Titanium Alloys

In recent years examination of thin foils of metals and alloys has been widely used in studies of deformation and phase-transformation mechanisms. Applications of this technique to studies of titanium and titanium alloys have been infrequent. Therefore, as a large number of titanium alloys have been investigated in this laboratory, it is proposed to give an account of methods used. Particular emphasis will be placed on some of the artifacts introduced in thin foils of titanium and titanium alloys during preparation. Experimental Procedure. It has been found that a large number of titanium alloys can be electropolished in a solution consisting of 30 cu cm perchloric acid (60 pct), 175 cu cm n-butyl alcohol, and 300 cu cm methyl alcohol. Thin foils are prepared using the window method and the electropolishing conditions listed in Table I. Although this solution is not unique, it is attractive because of its low concentration of perchloric acid and the wide range of alloys for which it can be used. Electropolishing is conducted at below -25°C as above this temperature a brown anodic film is produced on the specimen surface. Temperatures above -25°C also accentuate preferential attack of the 0 phase in the two-phase alloys, which unfortunately occurs at all temperatures. Contamination. It is advantageous to reduce the specimen to a thickness of 25 to 50 p prior to electropolishing, since the low-temperature electropolishing technique results in a low rate of metal removal. Both chemical polishing and grinding have