Part IV – April 1968 - Communications - Structural Changes During Superplastic Deformation in AI-78 Wt Pct Zn Alloy

1 HE superplastic behavior of the eutectoid A1-78 wt pct Zn alloy has been thoroughly investigated by Back-ofen et al.' The superplastic elongations and the marked resistance to necking were rationalized in terms of high strain rate sensitivity. In a subsequent paper2 superplastic behavior was formulated to show Nabarro-Herring diffusional creep as rate controlling at low strain rates, giving way to a dislocation climb process at higher strain rates. In a paper devoted to an interpretation of superplasticity in two-phase alloys, Packer and sherby3 have included the results of an examination of the structure of an Al-Zn eutectoid specimen before and after superplastic deformation. No significant change in grain size or directionality was observed in the deformed microstructures. This one observation led the authors3 to suggest that con- tinuous recrystallization or grain boundary migration was responsible for superplasticity. The purpose of this note is to report our observations on the superplastic behavior of the Al-Zn eutectoid alloy which differ in certain respects from works previously reported. Following Hayden et al., the results are discussed in terms of dislocation climb as the important factor during superplastic deformation. A heat of nominally high (99.995) purity 22 wt pct A1-78 wt pct Zn was induction-melted and cast into a 0.5 by 6 by 12 in. slab. The slab was heated to 350°C and rolled to 1/8-in.-thick plate. The plate was then cold-rolled to 0.040-in. thickness, annealed at 35OaC, and rolled to the final thickness of 0.020 in.* Speci-