Part IV – April 1969 - Papers - An Investigation of the Formation and Growth of G. P. Zones at Low Temperatures in Al-Zn Alloys and the Effects of the Third Elements Silver, Silicon,and Magnesium

The formation and growth of Guinier-Preston zones in Al-Zn alloys containing 4.4, 6.8, 9.7, and 12.4 at. pct zn have been studied by the X-ray small-angle scattering method. Particular attention was paid to the effects of small amounts of third elements silver, silicon, and magnesium on the formation and growth of G.P. zones. It was noticed that an appreciable number of G.P. zones were formed during the course of rapid cooling and that the size, volume fraction, and number of these G.P. zones were influenced by the existence of the third elements. During subsequent aging it was also found that the addition of both silver and silicon lowered the temperature for the growth of G.P. zones, whereas the addition of magnesium raised it. These results were explained in terms of the mutual interactions among zinc atoms, vacancies, and the third elements. A number of studies on the formation and growth of Guinier-Preston zones in Al-Zn alloys have been reported.1-4 Panseri and Federighii have found that the initial stages of zone growth take place at temperatures as low as around -100°C. For investigation of the mechanism of the initial stages of zone growth, growth studies must be carried out at low temperatures. In order to investigate the possibility of the formation of G.P. zones by the nucleation mechanism or the spinodal decomposition during quenching which was reported by Rundman and Hilliard,5 the examination of the as-quenched structure must be performed. In this paper the investigation of the early stages of the formation and growth were determined by means of the X-ray small-angle scattering method. With this technique, change of X-ray scattering intensities was measured while quenched specimens were heated slowly from liquid-nitrogen temperature to room temperature. At as-quenched state and after heated to room temperature, investigation of zone size, volume fraction, and zone number per unit volume was carried out. Measurements on these specimens yielded information on the early stages of zone formation and growth. Measurements were made also on specimens quenched to and aged at room temperature. From these measurements the previously reported model6 for the later stages of growth is confirmed; namely, the larger zones grow at the expense of smaller ones. Three elements, silver, silicon, and magnesium, were chosen as the third elements for the following reasons: Silver. In the binary A1-Ag alloy the spherical disordered 77' zones were observed immediately after quenching.7 Therefore, in the Al-Zn-Ag alloys, it is suggested that silver atoms might induce cluster formation during quenching. Also, since the migration energy of the zinc atoms was found to be raised by the addition of silver atoms,' silver atoms may have a great effect of the zinc diffusion, especially during low-temperature agings. Silicon. The effects of the addition of silicon atoms were found to be marked, especially at low-tempera-ture aging. In the binary Zn-Si system, no mutual solid solubilities between silicon and zinc9 and no in-termetallic compounds10 are reported to exist. Shashkov and Buynov11 investigated the behavior of silicon atoms in Al-Zn alloys and showed that silicon was not in the G.P. zones. The interaction between silicon atoms and vacancies is strong enough to increase the quenched-in vacancy concentration.* Magnesium. Magnesium atoms are reported to trap quenched-in vacancies and after much longer aging times these trapped vacancies will become free and act as diffusion carriers.13 Therefore at intermediate aging times, the diffusion of zinc atoms in Al-Zn-Mg alloys will be slower than in the binary Al-Zn alloys, whereas at longer times zinc diffusion will become faster. EXPERIMENTAL PROCEDURE The alloys used in this investigation had compositions of 4.4, 6.8, 9.7, and 12.4 at. pct Zn with or without 0.1 and 0.5 at. pct Ag, Si, or Mg. The alloys were prepared from high-purity aluminum, zinc, silver, silicon, and magnesium, with each metal having a purity better than 99.99 pct. The analyzed composition of the specimens is given in Table I. The measurements of the X-ray small-angle scattering were carried out with foils of 0.20 mm thick. The change of the scattering intensity was always measured at the fixed scattering angle of 20 = 2/3 deg. This angle exists nearly on the position of the intensity maximum. The value of the interparticle interference function14 which has large effect in this range of angles may not change abruptly in the case of the spherical shape of small zones. Therefore, from the above considerations, it is concluded that an increase of the intensity measured at this constant angle corresponds to an increase of the average radius and volume fraction of G.P. zones. The specimens were homogenized at 500°, 450°, and 300°C for 1 hr in an air furnace. For the study of the formation and growth at low temperatures, the foil