Part IV – April 1969 - Papers - Transformation Strain in Stressed Cobalt-Nickel Single Crystals

The influence of an external stress and plastic deformation on the allotropic transformation of single crystals of a Co-30.5 pct Ni alloy was investigated. Experimental results were obtained from dilatometry, X-ray diffraction, and optical and electron microscopy. The effects of stresses could be conveniently divided into three stress ranges. In range I, from 0 to about 400 g per sq mm, the specimens exhibited a multi-variant phase change on cooling and a considerable amount of retained cubic phase. In range II, from 400 g per sq mm to the elastic limit, hexagonal regions of a given orientation grew in size and the cubic phase disappeared with increasing stress level. In range III, just above the elastic limit, specimens transformed into hexagonal single crystals. It was found that plastic deformation, not applied stress, was the factor which determined whether a single-crystal product was formed. The observed macroscopic shear directions were mainly (112) on cooling, but the behavior was more complicated on heating under stress. To explain these properties of the phase change, a model based on the nucleation of partial dislocations is proposed. IT is well-known1 that, on heating, hcp cobalt transforms into an fcc arrangement by shearing on close-packed planes. The crystallographic orientation relationship of the phases is as follows: the habit plane is (OOO1)hcp ?{lll}fcc and a (1010)hcp direction is parallel to a (112)fcc direction. The temperature at which the transformation occurs in pure cobalt is around 420.C 1,2This temperature decreases with increasing nickel concentration: and at about 30 pct Ni it reaches room temperature. However, many of the transformation characteristics remain essentially the same, particularly the crystallographic features.495 A convenient way of studying the transformation is to alloy cobalt with nickel, thus avoiding the difficulties of doing experiments at the high temperatures needed to transform pure cobalt. Due to the hysteresis of the transformation it is possible to choose a Co-Ni alloy with an Ms temperature below room temperature and an A, temperature above room temperature. Either structure of such an alloy could then be studied at room temperature, depending on whether it had just been heated or cooled to room temperature. The choice of nickel is further favored by the small difference in lattice parameters between cubic cobalt and nickel and the similarity of their physical, chemical, and electronic properties. Co-Ni alloys are reported to have neither long- nor short-range order.6 The main purpose of this work was to investigate the influence of an external stress on the transformation characteristics of Co-Ni single crystals. It may be expected that slip, twinning, and transformation should have many features in common in cobalt, because the (111) planes of the cubic phase operate as slip planes when plastic deformation by slip occurs, they are the twinning planes, and they are the habit planes for the transformation. Many previous investigators7-&apos;6 have concluded that dislocations must play an important role in the nucleation and propagation of the transformation, just as they do for slip and twinning propagation. An external stress will affect their motion, and a study of its influence should yield further information about the atomic mechanism of transformation. The present work extends that of Gaunt and christian17 and Nelson and Altstette18 in both qualitative and quantitative effects of stress. The basic concept underlying all the present theories of the transformation of cobalt and Co-Ni alloys is the motion of a/6<112> partial dislocations over {1ll} planes of the cubic lattice. The ABCABC... stacking of the close-packed planes of the cubic phase can be changed into the hexagonal ABABAB... stacking by the sweeping of an a/6 <112> partial on every second plane. Twinning, on the other hand, requires a shear of a/6 <112> on each close-packed plane. The reverse transformation can be effected in a similar way by a/3 (1010) dislocations moving over every other basal plane of the hexagonal phase. Transformation theories2, 7- 12,14 differ in the details of the nucleation of the transformation and the propagation of the partial dislocations from plane to plane. EXPERIMENTAL PROCEDURE Nickel and cobalt rods supplied as 99.999 pct pure were induct ion-melted together under a vacuum of about 10-5 torr in a 97 pct alumina crucible. An alloy containing 30.5 pct Ni was found to have the desired transformation range, with an Ms near -10°C and an j4s in the vicinity of +10O°C. The ingots were swaged to &--in. rod and electron beam zone-leveled in a 10-6 torr vacuum. This procedure resulted in 12-in.-long single fcc crystal rods (designated I to VII) from each of which several tensile specimens of identical orientation were made. Chemical analysis of the bar ends indicated no contamination or gross segregation and no micro segregation was seen in electron micro-probe scans. Tensile specimens with a 9/32-in.-sq by 1-in.-long gage section were spark-machined from the rods and then electropolished or chemically polished to remove the machining damage and to provide a flat surface