Part IX – September 1968 - Papers - The Catalyzed Oxidation of Zinc Sulfide under Acid Pressure Leaching Conditions

The iilzfluence of catalytic agents on the oxidation of ZnS has been studied under pressure leaching conditions, using a chemically prepared sample of ZnS which was substantially unreactive on heating at 113°C with dilute sulfuric acid and 250 psi oxygen. Nurnerous prospective catalysts were added at the ratio of 0.024 mole per mole ZnS in the above reaction but pvonounced catalytic activity was confined to copper, bismuth, rutheniuwl, molybdenum, and iron in order of. decreasing effectiveness. In the absence of acid, where sulfate was the sole product of oxidation, catalysis was exhibited by copper and ruthenium only. Parameters affecting the oxidation rate were catalyst concentration, temperature, time, oxygen pressure, and a7riount of acid, the first two being most important. The main product of oxidation in the acid reaction was sulfur, with trinor amounts of sulfate. An electrochemical (galvanic) mechanism has been suggested for the sulfuv-forming reaction, whereby the relatively inert ZnS is "activated" by incorporation of catalyst ions in the lattice and the same catalysts subsequently accelerate the reduction of dissolved oxygen at cathodic sites on the ZnS surface. Insufficient data was obtained to Provide a detailed mechanism for sulfate fornzation, which is favored at low acidities and probably proceeds th'rough intermediate transient species not identified in the preseni work. THE oxidation of zinc sulfide at elevated temperatures and pressures takes place according to the following simplified reactions: ZnS + io2 + H2SO4 — ZnSO4 + SG + HsO [i] ZnS + 20,-ZSO [21 In dilute acid both reactions occur but Reaction [I] is usually predominant, whereas in the absence of acid only Reaction [2] can be observed. Both proceed very slowly with chemically pure zinc sulfide but can be greatly accelerated by the addition of suitable catalysts, as suggested by jorling' in 1954. Nevertheless, an initial success in the pressure leaching of zinc concentrates was achieved by Forward and veltman2 without any deliberate addition of catalytic agents and it was only later that the catalytic role of iron, present in concentrates both as (ZnFe)S and as impurities, was recognized and eventually patented.3 It is now apparent that another catalyst, uiz., copper, may have also played a part in the successful extraction of zinc, since copper sulfate is almost universally used as an activator in the flotation of sphalerite and can be adsorbed on the mineral surface in sufficient amount The importance of catalysis in oxidation-reduction reactions such as those cited above has been emphasized by various writers and Halpern4 sums up the situation when he writes that "there is good reason to believe that such ions (e.g., Cu) may exert an important catalytic influence on the various homogeneous and heterogeneous reactions which occur during leaching, particularly of sulfides, thus affecting not only the leaching rates but also the nature of the final products." Nevertheless relatively little work has appeared on this topic, one of the main reasons being that sufficiently pure samples of sulfide minerals are difficult to prepare or obtain. When it is realized that 1 part Cu in 2000 parts of ZnS is sufficient to exert a pronounced catalytic effect, the magnitude of the purity problem is evident. An incentive to undertake the present work was that an adequate supply of "pure" zinc sulfide became available. When preliminary tests established that the material, despite its large surface area, was substantially unreactive under pressure leaching conditions, the inference was made that it was sufficiently free from catalytic impurities to be suitable for studies in which known amounts of potential catalytic agents could be added. The first objective in the following work was to identify those ions or compounds which accelerate the reaction rate and, for practical reasons, to determine the effects of parameters such as amgunt of catalyst, temperature, time, acid concentration, and oxygen pressure. The second and ultimately the more important objective was to make use of the experimental results to further our knowledge of the reaction mechanisms occurring under pressure leaching conditions. The fact that catalysts can dramatically increase the reaction rate suggests that physical factors such as absorption of gaseous oxygen, transport of reactants and products, and so forth, are not of major importance under the experimental conditions employed and an opportunity is thereby provided to concentrate on the heterogeneous reaction on the surface of the sulfide particles. As will appear in the sequel, the first of these objectives has been achieved in a semiquantitative fashion but a great deal still remains to be clarified in the field of reaction mechanisms. EXPERIMENTAL a) Materials. The white zinc sulfide used was a chemically prepared "Laboratory Reagent" material (B.D.H.) and X-ray diffraction tests showed it to contain both sphalerite and wurtzite. The specific surface area, measured by argon absorption at 77"K, varied between 3.9 and 4.6 sq m per g. Analysis gave 65.0 pct Zn (67.1 pct theory) and 31.9 pct S (32.9 pct theory). Other metallic sulfides (CdS, FeS, and so forth) used in the experiments were also chemical preparations of "Laboratory Reagent" grade. Samples of mar ma-