Part V – May 1969 - Papers - Thermodynamic Analysis Of Dilute Ternary Systems: Ill. The Au-Cu-Sn System

Heats of solution of gold and copper in dilute Au-Cu-Sn alloys have been determined using a liquid metal solution calorimeter. The self-interaction coefficient, Au - has been calculated at constant copper concentrations and n cu has likewise been determined at constant gold contents. Good experimental agreement is obtained between the interaction coefficients and nAu Cc thus demonsbating the reliability of the measured heat values. The measured data are compared with the Predictions of certain solution models. In previous publications,1,2 the results of calori-metric investigations of dilute Ag-Au-Sn and Ag-Cu-Sn alloys have been presented. The present work on the Au-Cu-Sn system concludes a program of studies of enthalpy interaction coefficients in dilute alloys of the Group IB metals with tin. Since the definition and derivation of an enthalpy interaction coefficient has been discussed previously,1,2 no restatement of this theory will be presented here. From the determination of the partial heat of solution of gold and copper in ternary alloys of various copper and gold contents, values of the interaction coefficients can be calculated. These coefficients give an insight into the various solute interactions that occur in the liquid solutions since changes in their magnitude and sign reflect bonding changes that are taking place in alloys of varying solute contents. EXPERIMENTAL Details of the design and operation of the liquid metal solution calorimeter used in this work may be found in a paper by Poo1.3 For the present studies copper of 99.999 pct purity was supplied by American Smelting and Refining Co., gold of 99.999 pct purity by A. D. Mackay, Inc., and tin of 99.99 pct purity by Baker Chemical Co. At the commencement of each series of experimental drops, a tin solvent bath consisting of between 70 and 90 g of the pure metal was inserted in the calorimeter. The weight of the bath was accurately determined and to it were added appropriate amounts of gold or copper to give alloys of the desired composition. For determinations of approximately 0.0015 g-atom samples of Cu were used and for measurements of ?HAu approximately 0.0025 g-atom additions of Au. The heat capacity of the bath was determined at regular intervals during a series of drops using tin calibration samples. Measurements were made of the heat of solution of copper in alloys containing a constant 0.01, 0.02, 0.03, and 0.04 mole fraction of Au, respectively, in order to determine ?HCu in each alloy, and the same mole fractions of copper were used to determine equivalent values for nAu at constant copper concentrations. The composition of the bath was maintained at the desired constant gold or copper content by making calculated additions of the appropriate solute throughout the experiments. The limiting values ?HAu in alloys of constant copper content and of %c, in alloys of constant gold content were studied as a function of the mole fraction of copper or gold respectively in order to determine and nCu. Heat content and heat capacity data used in calculating values of ?ºHAu and ?HCu at the experimental temperature of 720°K were obtained from Hultgren et a1.4 ' RESULTS AND DISCUSSION Determinations of ?HAu. The partial heat of solution of gold in pure tin as a function of gold concentration was determined in the previous study of dilute Ag-Au-Sn alloys1 and can be represented by the least-squares expression: ?HAu(l) =-8075 + 2413xAu [l] which is valid between XAu= 0.00 and xAu = 0.05. The standard error in the constant term, which represents the partial heat of solution of gold at infinite dilution in tin,?HºAu(l)is 35 cal per g-atom, while the standard deviation of the slope, which represents n Au is ± 619 cal per- agtom. Corresponding expressions for ?HAu(l) in alloys containing constant mole fractions of 0.01, 0.02, 0.03, and 0.04 copper were obtained from the data listed in Table I and are themselves given in Table II. Fig. 1 illustrates the partial heat of solution of gold as a function of its concentration in each of the alloys. For the four alloys of constant copper concentration, the values obtained for ?HºAU(l) (in order of increasing copper content) are -8141 i 36 cal per g-atom, -8210 ± 42 cal per g-atom, -8202 ± 46 cal per g-atom and -8268 ± 51 cal per g-atom. The corresponding values of the self-interaction coefficient, n Au, for these alloys are 3103 * 644 cal per g-atom, 2425 ± 676 cal per g-atom, 2574 * 717 cal per g-atom and 2523 ± 899 cal per g-atom. In Fig. 2 these values of n Au are plotted as a function of the copper content of the alloys and are seen to remain approximately constant within the experimental limits. The addition of increasing, small amounts of copper to dilute binary Au-Sn alloys thus has no apparent effect on Au-Au interactions in these dilute liquid solutions, although more exothermic values of ?HºAu(l) do result from an increase in the copper content of the alloys. Analogous behavior was observed with additions of silver to dilute Au-Sn alloys.' By