Part VI – June 1968 - Papers - Kinetics of the Thermal Decomposition of Tungsten Hexacarbonyl

The mixed homogeneous and heterogeneous kinetics of the thermal decomposition of tungsten hexacarbonyl were studied by employing a batch reactor. The system was such that a sample of tungsten hexacarbonyl could be injected into the preheated reactor, and the progress of the reaction followed by a simple pressure measurement. Both the homogeneous and heterogeneous reactions were found to be first order, and approximate activation energies were determined for each reaction. It is shown that the dis-proportionation of carbon monoxide to give carbon and carbon dioxide cannot be the source of carbon in tungsten deposits prepared by this reaction. The kinetics of the thermal decomposition of tungsten hexacarbonyl have been investigated as part of a continuing study by the U.S. Bureau of Mines on the decomposition of organometallic compounds. Reactions involving the thermal decomposition of metal carbonyls have a potential application in the preparation of pure metals and fine metal powders. Indeed, it was these applications which provided the impetus for much of the early work involving the carbonyls of nickel1 and iron.' The relative lack of study of other metal carbonyls can be traced to the comparative difficulty in synthesizing these compounds. The most common use for tungsten hexacarbonyl has been as an intermediate in vapor-phase plating.7'8 However, attempts to obtain a carbon-free deposit of tungsten by this method have not been successful, and some investigators have taken advantage of the carbon contamination and used this process to form tungsten carbide deposits.lo Other investigators have studied the thermodynamic properties11"14 and molecular structure of tungsten hexacarbonyl. However, very little is known about the kinetics of this thermal decomposition, the mechanisms involved," or the source of carbon in the resulting plate. In contrast, studies have been made of the kinetics of the thermal decomposition of nickel tetracarbonyl, iron pentacarbonyl, and molybdenum hexacarbonyl.'l It has been found that these thermal decompositions occur by a mechanism which is partially heterogeneous in nature. Information available on the equilibrium constants for the decomposition of tungsten hexacarbonyl was used to determine a temperature range, 500" to 560°K, in which the reaction could be expected to be essentially complete. APPARATUS The apparatus used allowed the injection of a sample of tungsten hexacarbonyl into a preheated batch reactor and the use of a simple pressure measurement to follow the progress of the reaction in the sealed reactor. The pressure was sensed by means of a pressure transducer (Consolidated Electrodynamics Corp., 0.3 pct)* capable of operating at the *Reference to specific products is made to facilitate understanding and does not imply endorsement of such brands by the Bureau of Mines._______ reaction temperature. This type of sensing element was chosen to avoid the problem of condensation of the sublimed carbonyl in the capillary tubing leading to any type of remote pressure-sensing device. stirring was provided by rotating the entire apparatus. Glass beads placed in the reactor provided a pulsating agitation. To minimize thermal gradients in the reactor walls, the reactor was constructed of aluminum. The support tube which held the reactor in the furnace was thin-walled stainless steel to minimize heat conduction out of the reactor. As a result of these measures, a nearly uniform temperature (°C) was maintained throughout the reactor. Fig. 1 is a schematic diagram of the apparatus. The small gear motor rotated the entire apparatus at about 200 rpm. The bearings shown at the ends of the air cylinder were perforated to allow air to be fed to the charging piston and to allow inert gas to be fed to the reactor during the preheating period. The sample was simultaneously injected and sealed inside the reactor by operation of the air piston. Fig. 2 shows a cross section of the air cylinder and the adjoining portion of the support tube leading to the reactor. The sample carrier is shown in place at the right-hand end of the injection rod extending from the air piston. The piston is shown in the retracted position, as it would be prior to the start of an experiment. The small Teflon gasket which encircled the sample carrier at the end of the injection rod sealed the reactor when the sample was injected. This seal was maintained throughout the test by maintaining air pressure on the piston. The sample carrier was a 2-in. section of thin-walled, -in.-diam nickel tubing with an internal blank about 1 in. from the base and with the base end sealed.