Part VI – June 1968 - Papers - On the Nature of the Chill Zone in Ingot Solidification

The surface structure and substructure of Al-Cu alloys solidified as conventional ingots and under particular conditions such as those used by Bower and Flemings are studied. The influence of lampblack coating on the mold walls is especially considered and the results compared with those obtained in copper and graphite molds where no coatings exist. When high heat extraction conditions exist the observations show that mechanism of copious nucleation is responsible for most of the chill zone. When the heat extraction through the mold walls is low, a coarse grain structure with dendritic morphology arises, with a size that depends on the degree of convection present, analogous to that analyzed by Bower and Flemings. In both cases the effect of the convection on the macroscopic and microscopic appearance is discussed. The ingot macrostructure consists of one or more of three zones: "chill zone", "columnar zone", and central "equiaxed zone". The mechanism of the columnar-equiaxed transition has been subject of considerable interest and at present at least three theories exist about the formation of the equiaxed region: 1) the constitutional supercooling theory1 maintains that the equiaxed crystals nucleate after the columnar zone has formed, as a result of the constitutional supercooling of the remaining liquid; 2) chalmers2 pointed out, however, that there were several objections to this proposal, and that consideration should be given to the possibility that all the crystals, equiaxed as well as columnar, originated during the initial chilling of the liquid layer in contact with the mold; 3) Jackson et aL3 and O'Hara and ~iller~ suggested that a remelting mechanism of the dendrite arms is responsible for the formation of the equiaxed region. After the work of Cole and Bolling and other authors6 it became evident that convection (natural, reduced, or forced) plays a very important role in the transition from columnar to equiaxed and on the size of the resultant equiaxed structure. Until recently the accepted explanation of the chill zone was that it occurs as a result of copious nucleation in the liquid layer in contact with the mold walls.798 The columnar region is a subsequent result of the growth of favorably oriented grains and, as a result of a selection mechanism studied by Walton and Chalmers,9 elongated grains with marked texture are formed. Recently, however, Bower and Flemings" using an ingenious laboratory experiment introduced the idea that the "copious nucleation" mechanism is not responsible for the formation of the chill zone and that the presence of convection, introducing some form of "crystal multiplication", plays a decisive role in the formation of the chill zone. Unfortunately, it is important to consider that for their conclusions Bower and Flemings extrapolated the results obtained in their special experiments to the case of conventional ingots, and that these authors only analyzed the macrostructures of the specimens. Let us consider the work by Biloni and chalmers" concerning predendritic solidification. These authors were able to show that a study of the segregation substructure of A1-Cu gives information about the nucleation and growth of crystals formed in contact with a cold surface. A spherical predendritic region characterizes the first part of every grain nucleated in contact with the surface as a result of the chill effect. The aim of this paper is to elucidate through the observation of the segregation substructure the conditions under which (in the Bower and Flemings type of experiments and in conventional ingots) either the nucleation or the multiplication mechanism gives rise to the structure in contact with the mold walls. I) EXPERIMENTAL TECHNIQUES The experiments were performed on two alloys: Al-1 wt pct Cu and A1-5 wt pct Cu. The purity of the aluminum was 99.99 pct and the copper 99.999 pct. The results obtained with both alloys were similar. In the Bower and Flemings type of experiments the apparatus employed to obtain rapid solidification against a surface was similar to that used by those authors. The liquid was drawn by partial vacuum into the thin section mold cavity. Plate casts were 5 cm wide and usually 7.5 cm high. The thicknesses of the cast were 0.1 and 0.3 cm. Two different materials were used for the mold, copper and nuclear-grade graphite. The internal mold surfaces were polished and left uncoated for some experiments. In other experiments, the copper or graphite surface was coated with a thin film of lampblack material. In some of these particular experiments one of the mold walls was left with an uncoated region (usually in the form of a cross). The conventional ingots were cast in graphite or copper molds. In different experiments the mold walls were sometimes uncoated or coated with lampblack material. The results obtained in conventional and Bower and Flemings copper molds were compared with those obtained with copper molds coated with a very thin film of graphite; the results obtained were essentially similar. The size of the conventional ingots was 5 cm diam and 7 cm high in all cases. The cast surfaces produced by the Bower and Flemings type of experiments and conventional methods were observed macroscopically and microscopically without any metallographic preparation. As Biloni and Chalmers showed," the observation of the chill surface can give considerable information about the structure and segregation substructure.