Part VII – July 1968 - Papers - Grain Boundary Penetration of Niobium (Columbium) by Lithium

Oriented, oxygen-doped niobium bicrystals were tested in liquid lithium. The grain boundaries were attacked preferentially. The depth of the penetrated zone varies as (time)2. The penetration was aniso-tropic, had a high activation energy, and increased with the increased oxygen doping level. A possible model was proposed to account for the experimental observations. 1 HE grain boundary penetration of a metallic system by liquid metal has been studied by several investigators. Their results are summarized by Bishop.' Most of these works show that the penetration by liquid metal corresponds to the phenomenon of liquid metal wetting. In the case of a grain boundary, wetting will occur when twice the solid-liquid interfacial tension is smaller than the grain boundary tension resulting in the replacement of the grain boundary by two new solid-liquid interfaces. Other possibilities exist; for example, the atoms of the liquid metal may diffuse into the grain boundary region due to chemical potential gradient. The gradient can be produced by impurity segregation or simply be due to the increase in solubility in the grain boundary region. The penetrated grain boundary in these cases may remain solid at the test temperature. The Nb-Li system has been of considerable interest because of its possible technological applications. For fundamental interest it provides a possibility of studying the grain boundary penetration process which is not controlled by the wetting mechanism. The pure niobium is not attacked by the liquid lithium, but if niobium containing more than 300 to 500 ppm oxygen by weight is exposed to liquid lithium, corrosion occurs at the solid-liquid interface and preferentially at grain boundaries. Previous investigators2-' have proposed that this preferential corrosion at grain boundaries is caused by oxygen segregation there, with subsequent inward diffusion of lithium to form a Li-Nb-0 compound. These investigators also found that the corrosion could be retarded by adding 1 pct Zr to the niobium to precipitate the oxygen as ZrO2 upon proper heat treatment. However, there are no quantitative data on the kinetics of the grain boundary penetration process to test the validity of the proposed corrosion mechanism. In this work an investigation of this penetration process in oriented bicrystals was made as a function of the oxygen doping level in the bulk niobium and the grain boundary orientation. A possible model for the penetration process based on the experimental results was proposed. EXPERIMENTS Oriented niobium bicrystals were grown by arc-zone melting oriented single-crystal seeds.7 These bicrystals contained simple tilt boundary. The [001] directions in the two grains were tilted about a common [110]. The bicrystals were 31/2 in. long and 5 by 4 in. in cross section with the straight, symmetric, planar grain boundary longitudinally bisecting the crystal rod. The bicrystals were doped with oxygen by anodically depositing a layer of Nb2O on the surface in a 70 pct HNO solution at 100 v, using a stainless-steel cathode. The specimens were homogenized by annealing in evacuated quartz tubes at 127 5°C. Oxygen content of the niobium was measured from microhardness values, after DiStefano and Litmman.' Supplementary checks were made with vacuum-fusion analysis.7 Individual test specimens cut from the doped bi-crystal rods, about by by % in. in size, were tested inside double jacket sealed capsules. The inner jacket was niobium, the outer was stainless steel. The niobium inner jacket eliminated the problem of dissimilar-metal mass transfer.' The lithium (99.8 pct pure, obtained from Lithium Corp. of America) was handled only in a purified argon atmosphere in a Blickman stainless-steel glove box. After introduction of lithium, the capsules were sealed by welding. Further detailed experimental procedures are given in Ref. 7. The capsules were heat-treated in vertical Marshall resistance furnaces. Temperatures were controlled to When heating above 1100°C, it was necessary to seal the furnace work tube and flow argon through to prevent failure of the stainless-steel outer jacket of the capsule. Tests were made on 6" 2", 16" 2, and 33" i2" bicrystals at oxygen levels up to 2600 ppm by weight in the 6' and 16" crystals and with 1300 ppm oxygen in the 33' crystals. The oxygen levels were controlled to 100 ppm. Most of the quantitative data were obtained from 16" bicrystals between 800" and 1050°C. The capsules were quenched into water after the test and cut open with a water-cooled abrasive wheel. The capsules were then submerged in water, which dissolved the lithium and freed the specimen. Measurement of the depth of the penetrated zone in the grain boundary was done either on metallographically prepared surfaces or directly on the grain boundary plane after the specimen was fractured in tension in the grain boundary plane. The depth of penetration measured by both methods agreed well. Further details describing these techniques have been reported elsewhere.'p7