Part VII - Papers - Deformation of Silver-Zinc Single Crystals as a Function of Zinc Concentration

Stress-train curves were obtained for single crystals of silver, Ag-5 pct Zn, Ag-10 pct Zn, and Ag-20 pct Zn tested in tension and shear at 78°, 195°, and 297°K. At room temperature the critical resolced shear stress gC increased, the length of' the easy-glide region increased, and the rate of' work hardening dwving easy glide decreased with increasixg zinc concentration. The change in the ratio of uc at room temperature to that at lower temperatures was significantly greater for the alloys than for pure silver. It was found that an increment in stress was necessary to continue slip when the slip direction was rotated 60 deg. The magnitude of this increment increased with strain for all alloys, increased with zinc concentration for a given strain, and for a given strain increased with decreasing -temperature. DESPITE its practical importance in improving the mechanical properties, alloying is not fully understood. Except for copper alloys few sets of systematic data are available. Von Goler and Sachs' studied the deformation of Cu-Zn alloys of increasing zinc content and found that, for dilute alloys, the critical resolved shear stress increases linearly with concentration. The range of easy glide was found to increase with increasing zinc content. Schmid and seliger,2 Sachs and Weerts,3 and Osswald4 have shown that with Mg-A1, Au-Ag, and Cu-Ni crystals, respectively, the critical resolved shear stress also varies linearly with concentration. More recently, Linde and his coworkers have investigated the variation of the critical shear stress of copper alloyed with tin , antimony, indium, germanium, silicon, nickel, and gold. They found that the slope of the critical resolved shear stress is related to the change of lattice parameter with composition, and also to the difference in Goldschmidt's atomic diameter between solvent and solute atoms. Garstone, Honey-combe, and creetham6 have shown that similar relationships can be found for small additions of silver, gold, and germanium to pure copper. They found that, with increasing silver or gold concentration, the critical shear stress for glide is increased by alloying, and so is the range of easy glide, which reaches as much as 60 pct for 0.50 pct Ag alloy and 0.62 pct Au alloy, as compared to 6 pct for pure copper of similar initial orientation. They also found that the alloying additions had little effect on the rate of hardening during easy glide, the slope scarcely changing with increasing alloy content. General secondary slip was detected only when the crystals began to harden rapidly. Although the slip appeared to be very fine in the early stages of deformation, coarser slip bands were formed towards the end of the extensive easy-glide range. The present investigation describes the deformation characteristics of single crystals of Ag-Zn containing different concentrations of zinc. Tension and shear testing were used for this study. EXPERIMENTAL PROCEDURE The method of growing the single crystals, sample preparation, and method of testing have been described in detail previously.' EXPERIMENTAL RESULTS A) Tension-Room Temperature. The initial orientations and stress-strain curves of single crystals of silver, Ag-10.0 pct Zn, and Ag-20.0 pct Zn are shown in Fig. 1. It is evident that there is considerable change in the stress-strain characteristics as a function of zinc concentration. The effects of zinc concentration on the critical resolved shear stress for both CU-zn8 and Ag-Zn alloys are summarized in Fig. 2. At all concentrations the resolved shear stress of the Cu-Zn alloys is higher than that of the Ag-Zn alloys. The resolved shear stress increases parabolically as a function of composition for both alloy systems. The length of easy-glide region increased with increasing zinc concentration, Fig. 3b). As the length increased the slope (do/de) decreased slightly, Fig. 3(b). Metallographic investigations demonstrated two significant effects of increasing zinc concentration. First, the amount of clustering increased, compare Figs. 4(a) and (b). The slip lines changed from uniform in pure silver to clustered in the Ag-20 pct Zn and Ag-30 pct Zn alloys. Second, the amount of cross slip decreased as the amount of clustering decreased.