Part VII - The Thermodynamics of the Cerium-Hydrogen System

The Ce-H system was investigated in the temperature range, 573° to 1023°K, and the pressure range, 10-3 to 630 Torr, as a function of 'composition up to 72 at. pct H. Families of isothermal arid isopleth curves were plotted from the pressure-terr~perature-composition relationships. From these curves the solubility relationships were determined for the system. The isopleths are analytically represented by equilibrium dissociation pressure equations. The relative partial molal enthalpzes and entropies of solution of hydvogen in the systerrz were calculated fronz the dissociation pressure equulions and are tabulated. The integral free energies, enthalpies, and entropies of mixing in the Ce-H system were determined from the relative partial quantities and are also tabulated. The standard free energy, enthelpy, and entvopy of reaction of the dihydride phase at kcal per kcal per mole H2, and ?S° = -34. 1 cal per deg mole H2, respectively. The equilibrium dissociation pressure equation in the two-phase region is: UNTIL recently very little was known of the detailed solubility and thermodynamic relationships of the Ce-H system. Two previous investigations1,2 are noteworthy. However, significant discrepancies and omissions exist on analyzing them. The work of Mulford and Holley1 on cerium did not clearly delineate the boundaries of the two-phase region, Cess - CeH2-x. The plateau partial pressures were not thoroughly defined and were considerably displaced in pressure compared to those from the work of Warf and Korst.2 These latter authors concentrated their studies primarily from 823° to 1023°K in the pressure range of 1 to 760 Torr. No data were determined to outline the regions of primary solid solubility and the hydride phase. Also the establishment of the plateau partial pressures was rather limited in scope. In neither work was a treatment conducted of the relative partial molal enthalpies and entropies of solution of hydrogen in the single-phase regions and the integral thermodynamic quantities of mixing throughout the system. Therefore, it was the objective of this research to determine the complete equilibrium solubility relationships and thermodynamic data for the system by pressure-temperature-composition studies. EXPERIMENTAL PROCEDURE The cerium metal for this study was donated by the Reno Metallurgy Research Center of the Bureau of Mines. Total impurity content was 0.13 pct with only 60 ppm O. The metal was checked metallographically and contained only minor amounts of second phase compared to cerium from other sources. Specimen preparation was done in a dry box flushed with argon gas. The surface of a small rectangular piece of cerium (about 0.2 g) was filed with a clean, mill file. Final weighing was done in a tared enclosed vial containing argon gas. The specimen was then loaded quickly into the reaction chamber which was purged several times with high-purity hydrogen gas and then allowed to pump to about 10-6 Torr. The furnace was heated to the reaction temperature and the run started. The equipment used to conduct the hydriding was a Sievert's-type apparatus. Basically it consisted of a source for pure hydrogen, a precision gas-measuring burette, a heated reaction chamber, a McLeod gage, and a mercury manometer. Pure hydrogen was supplied by the thermal decomposition of uranium hydride. The 100-ml precision gas burette was graduated to 0.1-ml divisions and was used to measure the quantity of gas and admit it to the chamber. The reaction chamber was a quartz tube. Prior to each run, the cerium specimen was wrapped in a tungsten foil capsule to prevent reaction of the cerium with the quartz. Control of the temperature was achieved within ±1°K. Pressures in the manometer range were measured to ±0.5 Torr and in the McLeod range (10-3 to 5 Torr) to ±3 pct. The compositions of hydrogen in cerium were calculated in terms of hydrogen to cerium atomic ratio. These compositions were estimated to be ±0.01 H/Ce ratio. The technique used to study the equilibrium pressure-temperature-composition relationships of the Ce-H system was to develop experimentally a family of isothermal curves of composition vs pressure. The range of pressure through which each isotherm was developed was from 10-9 to about 630 Torr in the temperature interval, 573° to 1023°K. RESULTS AND DISCUSSION The hydriding characteristics of cerium are iso-morphous with those of the elements of the light-rare-earth group (lanthanum, cerium, praseodymium, and neodymium) wherein the region from the dihydride to trihydride is continuously single phase.' The structure of this phase is fcc.3 The heavy rare earths form a trihydride,2 which is hcp, separated by a two-phase region from the fcc dihydride phase. The Ce-H system is represented by the family of experimental isotherms in Fig. 1. Due to the small scale required to draw the curves, the experimental points are omitted; however, a total of 240 experimental data points were taken to prepare these curves. The solubility relationships can be deduced therefrom. Three distinct regions of partial pressure and composition can be seen. The region of cerium solid solution is represented by the rapidly rising isotherms in the dilute composition range. In accordance with Gibbs Phase Rule only one solid phase, the cerium solid so-