Part VIII - Thermodynamic Properties of Liquid Magnesium-Germanium Alloys

The thermodynamic properties of liquid Mg-Ge alloys have been determined between 1000°and 1500°K by an isopiestic method. Germanium specimens, heated in a temperature gradient and contained in covered graphite crucibles of special geometry, were equilibrated with magrtesium vapor in closed titanium tubes. The crucible design allowed free access of magnesium vapor to the samples during the equilibration to form alloys of magnesium and germanium, but prevented magnesium losses from the crucibles on quenching the titaniuin tubes to terminate the experimental runs, thus preserving the equilibrium alloy compositions. The activities and partial molar enthalpies of magnesium and the integral thermodynamic properties of the system were calculated from the experimental data. THE Mg-Ge phase diagram' shows one congruent melting compound, Mg2Ge, of essentially stoichio-metric composition, two eutectics, and very limited terminal solid solubilities. Very little information is available on the thermodynamic properties of the Mg-Ge system. The free energy of formation of Mg,Ge was recently deter-mined2 by a Knudsen cell technique in the temperature range 610° to 760°C. The standard enthalpy of formation of Mg,Ge was measured calorimetrically by Bever and coworkers.3 The present study was undertaken as part of a general investigation of the thermodynamic properties of the homologous series of Mg-Group IVB systems, i.e., Mg-Pb,4 Mg-Sn,5 Mg-Ge, and Mg-Si. An isopiestic technique was used which was developed by the authors5 for investigating the thermodynamic properties of liquid Mg-Sn alloys. Specimens of the nonvolatile component, contained in covered graphite crucibles, are heated in a temperature gradient in an evacuated and sealed titanium reaction tube, and equilibrated with magnesium vapor of known pressure. The method employs crucibles of special geometry which preserve the high-temperature equilibrium composition of liquid alloys having a highly volatile component such as magnesium on termination of the experimental runs by quenching the crucibles to room temperature. EXPERIMENTAL PROCEDURE First reduction germanium of 99.999+ pct purity (Eagle-Pitcher Co., Cincinnati, Ohio) and 99.99+ pct magnesium metal (Dominion Magnesium Ltd., Toronto, Canada) were used. The graphite crucibles were machined from high-density (1.92 g per cu cm) graphite rods (Basic Carbon Corp., Sanborn, N.Y.) which had a maximum ash content of less than 0.04 pct. The non-reactivity of graphite with germanium at the temperatures used in this study had been previously established by Scace and Sleck.6 The experimental procedure has been previously described in detail.5 The selection of a particular crucible geometry for a run was determined by a combination of imposed experimental conditions, the principle being that more tightly covered crucibles were required to preserve alloy compositions during quenching when higher magnesium pressures and higher specimen temperatures were used. Depending upon the composition range of the equilibrated alloys the source of the magnesium vapor was either pure magnesium or a two-phase mixture of Mg2Ge + Ge-rich liquid of known magnesium pressure. The experimental runs can be divided into the following three groups on the basis of crucible geometry and magnesium source material. Crucibles with Small Holes and Pure Magnesium Reservoirs. The crucible dimensions were identical to those of the Mg-Sn investigation5 except that the hole diameters were reduced to 0.010 in. because of the higher temperatures and higher magnesium pressures involved in the Mg-Ge system. During an equilibration run, magnesium vapor diffused from the reservoir to each specimen through the small holes, one drilled through the crucible lid and two others drilled through graphite baffles positioned vertically inside the crucible between the lid hole and the specimen. Since the magnesium pressure was high, i.e., in the range 117 to 277 Torr, during the equilibration time of approximately 24 hr, equilibration was not impeded by these holes. A specimen composition at equilibrium was fixed by the relative temperatures of the specimen and the reservoir, and by the thermodynamic properties of the system. Upon brine quenching the titanium reaction tube to end a run the vapor pressure of magnesium above the liquid alloys decreased exponentially with decreasing temperature, and the small cross-sectional areas of the holes (4.9 x 10"* sq cm) drastically reduced magnesium losses from the crucibles. Because of its low vapor pressure, germanium losses from crucibles during a run were at most 0.2 mg for pure germanium and correspondingly less for the alloys. This crucible geometry satisfactorily retained the equilibrium alloy compositions on quenching for magnesium-rich (from 3 to 33 at. pct Ge) alloys provided their temperatures were below the melting