Part X – October 1968 - Papers - High Damping Capacity Manganese-Copper Alloys. Part 1-Metallography

Four Mn-CLL alloys, containing 60, 70, 80, and 90 pct Mn, respectively, have been examined in the quenched and the quenched and aged conditions using electron microscopy and electron, neutron, and X-ray diffraction. After certain heat treatments the alloys transform from fee to fct and in the tetraom1 condition show a domain structure parallel to {101} planes. Neutron diffraction indicates that the domains are antiferrornagnetically ordered. The domain boundary contrast has been examined using bright- and dark-field microscopy, and the contrast effects observed under favorable conditions have been used to deduce the c axis orientation in each domain. The domains are extremely mobile and can be nucleated at precipitate particles and screw dislocations. The domain mobility is responsible for the high damping capacity. In the aged material a Mn precipitates in the Kurdjumov-Sachs orientation and results of both electron microscopy and neutron diffraction indicate that the matrix separates into two components—one rich in manganese and the other rich in copper. ALLOYS of manganese and copper have the unusual combination of a high damping capacity and good mechanical properties and have been the subject of a number of investigations as part of a general interest in high damping capacity alloys for engineering purposes.&apos;,&apos; SO far, however, there has been no reported electron metallographic study of these alloys. The Mn-Cu system has an extensive range of solid solubility at high temperatures, and the equilibrium phases are expected to be y (fee) and a Mn. The high damping capacity is associated with a metastable tetragonal structure of variable c/a ratio, which forms from the high-temperature y phase. This latter phase becomes more difficult to retain as the manganese content increases, and alloys containing more than 82 wt pct Mn undergo a reversible martensitic fcc — fct transformation on quenching. The X-ray work of Basinski and christian3 showed that the Ms temperature for the transformation was below room temperature for alloys in the range 70 to 82 pct Mn and increased linearly with manganese content. When quenched from the y region, alloys in the range 50 to 82 pct Mn are cubic at room temperature, but become tetragonal if aged at temperatures between 400" and 600°C. The martensite transformation occurs on cooling from the aging temperature. Tetragonal alloys have a banded microstructure and the bands analyze to be traces of (110) planes. Similar microstructures have been observed in In-Tl4 and in other manganese-base systems, such as Mn-Au5 and Mn-Ni.6 The mobility of the bands in Mn-Cu alloys can be demonstrated by optical examination of a polished specimen surface subjected to a cyclic stress.7 The bands appear and disappear as the stress is varied, and X-ray measurements of the (200,020) and (002) peak intensities confirm that a reversible reorientation of the tetragonal structure occurs. Meneghetti and sidhu8 investigated the magnetic structure of Mn-Cu alloys and found antiferromagnetic ordering in furnace-cooled alloys of composition >69 at. pct Mn. Magnetic super lattice reflections occurred at the (110) and (201) positions and the proposed structure was fct with the spins along the c axis. A more complete investigation by Bacon et al.9 confirmed this structure. The magnetic ordering temperature Tn was found to increase linearly with manganese content in the same way as the Ms temperature, and at any composition, Tn > Ms. This relationship suggested that the magnetic ordering was responsible for the cubic — tetragonal transformation in the manganese-rich alloys. The purpose of this investigation was to study the mechanism of high damping and the structural changes that occur on aging. The main technique used was transmission electron microscopy, but X-ray and neutron diffraction experiments were also carried out. EXPERIMENTAL Materials and Heat Treatment. The four alloys, provided by the Admiralty Materials Laboratory. were of nominai composition 60, 70, 80, and 90 Mn and all had low impurity levels, <0.05 pct C, <0.2 pct Fe. This material was cold-rolled to 200-µ strip with intermediate annealing and then given a final heat treatment of 24 hr in the range 800° to 900°C followed by water quenching. An identical heat treatment was given a length of 3/4-in.-diam bar of the 70/30 alloy from which the neutron diffraction specimens were machined. It was suspected that the tetragonal structures would be metastable at room temperature, and so the alloys were not aged until required for experiments. After aging in a salt bath the alloys were water-quenched. Thin Foil Preparation. Initial thinning to 50 to 75 µ was possible in a solution consisting of: 50 ml nitric acid 25 ml acetic acid 25 ml water The surface deposit and grain boundary etching was removed by a final electropolish at around 20 V in an electrolyte consisting of: