Part X – October 1969 - Communications - The Influence of Misfit on the Morphology and Stability of the Omega Phase in Titanium-Transition Metal Alloys

MANY aspects of the formation of the metastable w phase in titanium-transition metal alloys have been described in several recent papers.1-4 These papers have reviewed earlier work on the w phase and have further defined most of the important features related to the formation of this phase, e.g-., its crystal structure, composition, and morphology. There are, however, several important points regarding formation of the w phase in titanium alloys which have been described in less detail. Two of these are the relationship between lattice misfit and w phase morphology and the influence of lattice misfit on the mode of formation of the equilibrium a phase. In this communi- cation we will present transmission electron microscopy results relevant to these two points. The alloys used in this study were prepared by non-consumable electrode arc melting, each 30-g button being remelted a minimum of twelve times. The alloy compositions we have studied are listed in Table I. Thin foils were prepared using standard techniques described elsewhere. Two distinct c' phase morphologies have been reported in earlier papers. The phase is ellipsoidal in the Ti-Mo3 and Ti-Nbl system and cubical in the Ti-V3 system. Results of the present study show that the w phase is also cubical in Ti-Mn, Ti-Fe, and Ti-Cr alloys as illustrated in Fig. l(b) to (d). Fig. l(a) shows the ellipsoidal morphology in Ti-MO3 for comparison purposes. It was suggested in an earlier paper3 that the w phase morphology may be controlled by the lat-