PART XI – November 1967 - Papers - A High-Temperature Electromagnetic Stirrer

A high-temperature electromagnetic stirrer is described in which heating and stirring are accomplished by independently controlled power sources. The appavatus is suitable lor use at temperatures up to 1700°C in a variety of ambient atmospheres. Some typical examples of the homogenizatimz capabilities of the system are given. THERE are few processes in solidification that are not markedly affected by motion in the melt during freezing. In many instances, the mechanisms are diffusion-controlled, and the transport in the melt may be greatly accelerated by deliberately stirring the melt. In zone-refining, stirring1 assists the removal of rejected impurities from the interface, so the process proceeds at a faster rate. The transition from a planar to a cellular interface is caused by constitutional undercooling in the melt ahead of the interface: and stirring delays its onset. Stirring is valuable for homogenization of melts: and chemical reaction with sluggish kinetics may be accelerated. Finally, it has been observed that grain refinement is related to motion in the melt. Fine grain castings are usually produced by the addition of catalysts to the -melt,' catalysts which are thought to act simply as hetereogeneous nucleation centers. Even here motion is important. Richards and Rostoker 5 applied ultrasonic vibration to a solidifying A1-Cu alloy which had been innoculated with a catalyst and found that the grain diameter fell linearly with the amplitude, the peak acceleration and the power input to the melt from the transducer. Finally, mechanical and electrical stirring alone have been used to generate a fine-grained structure.6,7 Johnston ef a1.' have carried out a series of systematic investigations of grain refinement by electromagnetic stirring in a number of low melting point alloys. They found, for example, that the number of grains per unit volume in Pb-Sn alloys could be increased several orders of magnitude by stirring an undercooled melt at the moment of recalescence. In general, a relation AT .H = constant prevailed for a given grain size, where AT was the undercooling of the melt and H the field strength. In more recent work, deliberate homogeneous nucleation of slightly undercooled melts established that the mechanism of refinement must be one involving crystal fragmentation and subsequent multiplication, rather than a "shower" of nuclei effect.9 It is the purpose of this note to describe a stirring device suitable for use up to 1700°C. At low temperatures mechanical stirring and direct-current methods are feasible, but at high temperatures the problem of a protective atmosphere and of electrode corrosion rules out such procedures. The most convenient method for high temperatures is to use externally generated ac fields for both stirring and heating. With rf induction heating alone, considerable stirring and agitation can be achieved, but in general the penetration of field into the melt is small, and the stirring cannot be controlled independently of the heating. In the present experiments, separate power sources of different frequencies for heating and for stirring were used. A susceptor design was chosen so that the 450 kc rf heating field was completely absorbed in the susceptor. The stirring frequency, 400 cps, hereafter called the af field, was chosen so that a high penetration of the melt proper was achieved. EXPERIMENTAL APPARATUS The apparatus, Fig. 1, consists of a quartz tube and end plates, surrounded by an rf induction coil and six equally spaced af stirring coils, four of which are shown in full and a fifth in section. Each af stirring coil is a transformer of which the secondary is a single-turn water-cooled copper loop and the primary is composed of two 10 amp-117 v Variac cores as shown. These cores are cooled by forced air, as each of the six pairs will carry maximum currents of 15 amp for short periods. Each set of Variac windings are connected in series, but opposite sets are connected in parallel with a three-phase 400 cps 400-v source. By properly phasing the coils in this way, a rotating field is produced. Capacitors C1, C2, and C3 in Fig. 2 are used to match this inductive load to the generator. Fig. 3 shows a cutaway view of the quartz tube. The sample (1 in. diam by 1 in. high) is placed in a tapered alumina crucible. An axial W-26 pct Re thermocouple, enclosed by a protection tube, is provided. The cruci-