Part XI – November 1968 - Papers - The Density and Viscosity of Liquid Thallium

The density and viscosity of 1iquid thallium have been measured by absolute methods to temperatures of about 200° and 150°C, respectively, above the melting point. These new data reported, especially density data, do not closely confirm previous work. Density p, in g per cu Cm, is shown to vary linearly with temperaluve t, in °C, according to the equation p = 11.658 - 1.439 X l0-3t. The viscosity data obey the well-known Andrade equation nv1/3 = A exp C/vT , the constants A and C for thallium having values of 2.19 x A and 79.648, respectively. This paper reports some new data for the density and viscosity .of liquid thallium. Measurements of these fundamental physical properties were undertaken as part of a continuing research program at the Mines Branch, Department of Energy, Mines and Resources, Ottawa. Canada. A literature search has revealed that data are so scarce that there could not be a consensus on the true values of the density and viscosity of liquid thallium. To be more specific, there exists only one set of viscosity data' and only two acceptable sets of density data,273 one of which is limited in scope.3 In Liquid Metals Handbook,3 another density study is reported but indications of impurities in the thallium render the results suspect. In this situation, further careful experimentation was required to realize the true density and viscosity of thallium. EXPERIMENTAL METHODS Density. Densities were determined using a graphite pycnometer. The technique and its accuracy have been discussed in earlier papers.4'5 It is considered that experimental data can be obtained which are accurate within +0.05 pct, all sources of random and systematic errors having been evaluated. Density results for thallium were identical whether measured under an atmosphere of argon or a vacuum of 5 x 10-6 torr and, for the most part, the argon atmosphere was used. Viscosity. Viscosity measurements were made in an oscillational viscosimeter by an absolute method—the liquid metal being held in a closed graphite cylinder. Design and operation of the apparatus, constructed in this laboratory, have previously been discussed.6 For thallium, runs were made under a vacuum of about 2 x 10-6 torr. To evaluate viscosity coefficients from the various experimental parameters, the mathematical analysis of Roscoe7 was used. Measurements of the necessary parameters and the accuracy of these measurements have also been discussed.6 The cylinder dimensions were corrected for the anisotropic expansion of graphite, as discussed for density measurements.4,5 It is well-known that thallium oxidizes rapidly and hence a newly machined surface quickly tarnishes in air. The oxide film, however. is nonadherent and is easily removed by rubbing or by solution in water. Hence, immediately before use, both density and viscosity charges were immersed in water, wiped dry, and quickly transferred to the apparatus which was then rapidly evacuated. Specimens removed after determinations were only slightly tarnished and there was no other evidence that tarnishing affected the results. For example, the sharpness of the specimen edges from the containing vessels indicated complete filling by the liquid metal. Thallium of 99.999 pct purity was used in this investigation. Because of its high toxicity care was exercised in handling this material. For example, the melting procedure to prepare machinable ingots was carried out in an open, well-ventilated area, while protective gloves were always worn when handling the solid metal. RESULTS AND DISCUSSION Density. Measurements were made over a tempera-ture range of about 200°C above the melting point. The results are listed in Table I and plotted in Fig. 1. From the graph it is evident that the relation between density and temperature is linear. Such a relation has been observed before in this program for other metals and alloys475 and elsewhere by other workers. A least-squares analysis of experimental data gives the equation: pT1 = 11.658 - 1.439 x 10-3t where p = density in g per cu cm and t = temperature in "C. In Fig. 1, together with the present results, the data of Schneider and Heymer2 in the corresponding temperature range have also been plotted. Evidently, the two sets of data do not agree well, the results of Schneider and Heymer being about 0.6 pct higher. Viscosity. Viscosity data were obtained from the melting point, 303.5°C, up to 457.5"C. The data are listed in Table I and in Fig. 2 the plot of these results demonstrates a smooth curvilinear relation between