Physical Defects In Hollow Drill Steel

Small cracks in a plane normal to the axis of steels are found to be prevalent around the water hole of drill steels that have been in service for an unknown period of time. Cracks are not found on the exterior surface of the steels nor to any noteworthy extent even in the water holes of new drill steels. Undulations and serrations are found in the surface of the water hole in new steels; it is in the bottom of such defects that cracks appear to develop in used steels. The occurrence of the more serious of these cracks at the point in the steel to which it has been heated for forging or hardening is thought to account to a great extent for failures in that region. DURING the past, year, we have investigated the cause of 88 per cent, of the failures by breakage near the bit end of some 1-in. hollow, hexagon, drill steel used in a metal mine. This breakage in the region of the bit end of the steel was peculiarly interesting because we have been led to believe that breakage is most prevalent at the shank end of drill steels near the place where the steel is gripped in the chuck of the machine. Records from the mine showed, also, that the breakage was much more frequent in the short lengths of large gage than in the longer steels; this is shown graphically in Fig. 1. Because the shorter lengths of steels are usually those that have been made from broken pieces of long steels or from steels that have worn down in service, rarely being made from new stock, those who are wont to suspect steel of tiring and crystallizing in its old age through fatigue are quite apt to see in this instance an argument in favor of their idea. As usual, a careful examination of these steels reveals defects of a character hardly to be overlooked in favor of such a cause. The steel in question was rolled with a sand core and was of the usual drill steel composition: Carbon 0.85 per cent., manganese 0.60 per cent., silicon 0.25 per cent., phosphorus 0.02 per cent., and sulfur 0.02 per cent., with the exception that in some specimens there was vanadium, not exceeding 0.20 per cent.