Preparation And Characterization Of Fibrous Ni-Co Alloy Powders By Thermal Decomposition Of Solid Solution Of Complex Ni-Co Oxalates

Keywords: solid solution, Ni-Co alloy powders, thermal decomposition, fibres. Synthesis of fibrous Ni-Co alloy powders was achieved by thermal decomposition of precursor of complex Ni-Co oxalates solid solutions obtained via modified coprecipitation method among intimate mixing solution of NiCl2?6H2O , CoCl2?6H2O and H2C2O4?2H2O in the presence of surfactant polyvinylpyrrolidone (PVP) and organic solvent ethanol. Scan electron microscopy (SEM), X-ray diffraction (XRD), X-Ray photoelectron spectroscopy (XPS), disperse energy X-ray analyses (EDX) were used to characterize the structure features and chemical compositions of the as-prepared fibres. The influences of decomposition conditions, including temperature, time, the flow rate of N2+H2, and the heating rate, on the morphology, average size and specific surface area of the Ni-Co alloy powders were investigated. It is found that a trend of the mutual alloying of nickel and cobalt: the formation of perfect solid solution for any compositions NixCo100-x was indicated and corresponding NixCo100-x alloys with fcc phase can be obtained under the optimal conditions.