Preparation of MgO Whisker from Magnesite Tailings

China has abundant magnesite resource, but the low-grade and powder ores have always been rejected, which influences the comprehensive utilization of resource and often causes circumstance problems. The present work investigated the preparation of magnesia whisker using magnesite tailings as starting materials by preparation magnesium carbonate whisker as precursor firstly in the route of calcination, hydration, carbonation and pyrolysis, follows by second calcination of the precursor. The influence of pyrolysis conditions and additives on morphology of magnesium carbonate crystal as well as the influence of calcination conditions on morphology of magnesia whisker was investigated. The results showed that thermal decomposition products was MgCO3?3H2O. Magnesium carbonate whisker with length of 10~60 µm and the length-to-diameter ratio of 10~20 was prepared when soluble magnesium salt was added. While temperature was elevated at 1°C?min-1, magnesia whisker with length of 10~60µm was obtained.