Principle and Practice of producing Qualified Antimony White from Lead-Antimony Alloy by Blowing Directly

Base on the thermodynamic calculation of vapor pressure of lead, antimony and arsenic at high temperature, the possibility of separating lead, antimony and arsenic in different temperature was analyzed ,and the practice of producing qualified antimony white from lead-antimony alloy by direct blowing was introduced in detail in this paper. The blast furnace reduction smelting was brief introduced firstly, and then alkaline refining was applied to removing arsenic from lead-antimony alloy that contains As1%,Sb39%,Pb58%,the arsenic in the treated lead-antimony alloy could decrease to 0.009% by that method. The antimony white containing Sb2O3 99.5% could be produced by air blowing in the special furnace at 650? from the treated lead-antimony alloy. And the electrolytic lead could be achieved by electrolysis from the lead-rich alloy which contained 83% lead.With high-grade product being obtained the process was shortened. The technology has been applied successfully many years in Guangxi, China.