Processing and Properties of Hot-Pressed in-Situ Al(Tib2+Ah03) Metal Matrix Composites

"In-situ processes have emerged as new and promising techniques for metal matrix composite fabrication. They offer significant technical and economic advantages over conventional processing. One of the in-situ processing routes that have been used is reactive free sintering of a mixture of powder reactants. However, materials synthesised via this route are always porous because of density differences between reactants and products. An example are the porous Al/(TiB2+Ah03) MMCs obtained by heating powder mixtures of Al+ Ti02+B with Ti02 and B in stoichiometric ratios for forming TiB2• In this study, porous Al/(TiB2+Ah03) composites were further processed by hot-pressing at temperatures above 600°C. This processing cycle was designed so that the composites could be densified. Furthermore, the reaction kinetics of the in-situ processing are studied by means of DSC analysis measured at different heating rates. The activation energies of the three intermediate steps that are involved in the reactive processing for preparing AV(TiB2+Alz03) MMCs are determined to be 923 kJ/mole, 241 kJ/mole and 235 kJ/mole respectively.XRD proved that the hot-pressed products consist of Al, TiB2 and Al203- Properties of the products are assessed by microstructural characterisation (LOM, SEM and EDS), microhardness, Young's modulus and bending tests. The results show that good microstructures, elastic properties and strengths, as well as acceptable ductilities were achieved. For the composition 79.74wt% Al-15.95wt% Ti0z-4.31wt% B, after the reactive free-sintering and hot-pressing cycles, Young's modulus is 105 GPa, bending strength is 509 MPa and maximum strain is 5.0%; for composition 88.73wt% Al-8.87wt% Ti0z-2.40wt% B, they are 89 GPa, 311 MPa and 8.2% respectively. It can be seen that the properties of products can be tailored by adjusting the relative amounts of reactants in green samples. Furthermore, for comparison reasons, Al and a binary system Al-Ti02 were identically processed as the ternary systems. Their microstructures and properties were studied."