Producing–Equipment, Methods and Materials - Use of Oxygen Scavengers to Control External Corrosion of Oil-String Casing

This paper describes a laboratory study of causes of external casing corrosion and the test work that led to the use of oxygen scavengers to prevent this attack. External casing failures are classified as water-line, casing-casing, collar and body failures. A corrosion mechanism based on principles of differential oxygen availability is developed that is consistent with facts known about each kind of failure. The field use of oxygen scavengers is depicted as a direct result of the laboratory study. A part of the paper is devoted to reporting on the field use of hydra-zine to control external casing corrosion. Results of field measurements made over a period of several years are presented as evidence of the efectiveness of the hydrazine treatment. The first conclusion reached is that the use of hydrazine materially reduces the cathodic protection requirements for treated wells. This result is interpreted to mean that a reduction is taking place in the amount of corrosion on the casing. Results indicate also that hydrazine shows its greatest usefulness within the first 12 to 18 months after a well is completed when pitting corrosion is likely to be most active. INTRODUCTION According to surveys sponsored by the National Association of Corrosion Engineers,' the cost of repairing casing leaks caused by external corrosion may exceed $4 million per year. In addition, well damage and lost production resulting from casing leaks probably costs the petroleum industry an additional $5 to $6 million per year. Concern about the cost of external casing corrosion led to an extensive laboratory study of factors causing this external corrosion and to the development of a new approach to its prevention. This paper presents a discussion of various causes of external casing corrosion, details of laboratory studies and the results of the field use of an oxygen scavenger in well cementing fluids to prevent the external corrosion of oil-string casing. Measurements on test wells over a period of several years show that cathodic-protection current requirements are greatly reduced when hydrazine is used in cementing mud. Reduction of current requirements can be interpreted to mean that removal of oxygen by hydrazine has greatly suppressed corrosion cells on the external surface of the casing and thereby, has reduced corrosion. To date, hydrazine has been used by the Standard Oil Co. of California in more than 200 well completions. KINDS OF CASING FAILURES A survey of a large number of casing leaks disclosed four types of external casing failures — water-line, casing-casing, collar and body failures. These types are identified largely by their location on the casing. Water-line failures are found just below the surface of water or mud in the casing annulus. Casing-casing failures occur on the oil string just below the shoe of the surface string. Collar failures are found in the threaded ends of casing joints where they are screwed into casing collars. Body failures may occur at any point on the body of a casing joint. Ex- amples of each kind of failure have some of the general characteristics that are shown in Fig. 1. Water-line failures usually result in the circumferential severance of an oil-string casing. The corrosive action causing a water-line failure usually is sharply defined and is limited to a short length of the casing. Casing-casing failures usually are accompanied by pitting corrosion distributed around the oil-string casing for distances up to 100-ft below the shoe of the surface string. Casing-casing failures may also sever the casing. Collar failures seem to start on the first thread at the bottom of recesses between collar and casing joint. Corrosion proceeds across the threads by what appears to be a normal pitting mechanism. Both casing and collar are severely attacked. Body failures are the result of highly localized pitting at any point on a casing wall. Besides the pit that perforates a casing, a large number of other pits usually are found along one side of the casing joint. The pits occasionally are filled with corrosion products consisting largely of oxides and sulfides.' Frequently, the mill scale is largely intact on the rest of the casing. Examination of a casing failure does not always reveal the cause of the failure. Frequently, the necessary details are destroyed when the failure occurs. For example, formation water flowing through a perforation at high velocity may enlarge the hole and destroy any remaining evidence of the cause of the failure. One way to obtain undistorted information about a failure is to study the nature of other pits on the casing in the vicinity of the failure. A study of such pits frequently suggests that they are characteristic of an attack resulting from the differential availability of molecular oxygen.