Purification Effects of C2Cl6 on A00 Aluminum

The effects of several fluxes on purification, microstructures and properties of A00 aluminium have been studied. The experimental results and analyses indicate that many cracks and large porosities exist in the surface film above the melt purified by C2Cl6 and that the film is floe and mostly composed of AhO3 and pure aluminum, which carries many carbon particles and AlCh not fully volatilized. And then over 50% of the all-melting residue is pure aluminum, which is one of the major reasons for high melting loss. Moreover, because of a mass of gas bubbles and a state of seethe, there exist many inclusions which size is under l0µm in the microstructure of A00 aluminum purified with C2Cl6 or fluxes containing C2Cl6- With this purifying method, the aluminum crystal grains are extended along the radius that was observed firstly and the average crystal size of A00 aluminum are about 100µm~150µm. In addition, small size inclusions have little affected on tensile strength and micro inclusions under l0µm have little affected on elongation.