Relative Desulphurizing Powers Of Blast-Furnace Slags, II

IN a previous paper1 a method for the measurement of the comparative desulphurizing power of slags was described and data were presented covering the range of likely slags containing up to 10 per cent MgO In the present work the range is extended to include slags containing up to 20 per cent MgO, and the effect of temperature on 5 per cent and 15 pen cent MgO slags over the range 1475° to 1525° C is included The method used was that described in the previous paper except that some of the temperature measurements were made with a noble-metal thermocouple instead of a tungsten-graphite thermocouple Twelve-gram charges of 0 8 per cent sulphur-metal and 5-gram charge-, of slag were subjected to heating for 30 nun at a prescribed temperature The charges were analyzed for sulphur content For purposes of comparison, desulphurizing power is defined as the ratio of the percentage of sulphur found in the slag to that found in the metal Six slag and metal charges were made coincidentally in 5/8-in holes in a section of an electrode graphite rod One slag and metal charge was used as a control by means of which adjustment in the desulphurization value could be made for small variations in temperature and other factors For convenient presentation of the data, the slags are arranged in groups in each of which one of the four main slag components is constant Thus, the 15 per cent MgO slags are presented separately from those containing 20 per cent MgO SLAGS WITH MAGNESIUM OXIDE CONSTANT 15 Per cent MgO -The data on slags containing 15 per cent MgO cover a composition range of 24 to 50 per cent SI02, 5 to 27 per cent A1203 and 24 to 53 per cent CaO Variation in composition has been in steps of 2 per cent over much of the area Because the change in desulphurization power is generally gradual with gradual change in composition, certain sections have been covered m steps of 4I per cent and even