Relative Desulphurizing Powers of Blast-furnace Slags, II (296cc7cd-9fe7-4204-96ac-ebc021ac9c21)

IN a previous paper1 a method for the measurement of the compara-tive desulphurizing power of slags was described and data, were presented covering the range of likely slags containing up to 10 per cent MgO. In the present work the range is extended to include Tags containing up to 20 per cent MgO, and the effect of temperature on 5 per cent and 15 per cent MgO sings over the range 147.5° to 1525° C. is included. The method used was that described in the previous paper except that some of the temperature measurements were made with a noble-metal thermocouple instead of a tungsten-graphite thermocouple. Twelve-gram charges of 0.S per cent sulphur-metal and 5-gram charges of slag were subjected to heating for 30 min. at a prescribed temperature. The charges were analyzed for sulphur content. For purposes of comparison, desulphuriz-ing power is defined as the ratio of the percentage of sulphur found in the slag to that found in the metal. Six slag and metal charges were made coincidentally in holes in a section of all electrode graphite rod. One slag and metal charge was used as a control by means of which adjustment in the desulphurization value could be made for small varia-tions in temperature and other factors. For convenient presentation of the data, the slags are arranged in groups -in each of which one of the four main slag components is constant. Thus, the 15 per cent MgO slags are presented separately from those containing 20 per cent MgO.