RI 4879 Recent Practice At The Bureau Of Mines Boulder City, Nev., Titanium Plant

This paper discusses 105 production runs at Boulder City, Nev., in which titanium metal was made in 200-pound batches. It describes the equipment and techniques used in preparing raw material, the reduction process, and the removal of the reaction mass from the reaction vessel. Also, some data on man-hour requirements are presented. The main emphasis was on producing ductile-grade titanium and developing a standard procedure for obtaining a consistently pure product. Some departures from techniques used before were found to be desirable. The most important of these was the use of a sealed room with a controlled dry atmosphere in which the reaction vessel was opened and the reaction mass removed. This minimized the moisture taken up by the magnesium chloride in the reaction mass, and it could be purified successfully by vacuum distillation. Using the dry room also made it possible to leave al-inch shell of the reaction material on the walls of the vessel, which lowered the iron contamination and eliminated the labor and time-consuming job of cleaning the vessel after each reduction. Another change was lowering of the temperature during reduction to 750° C. instead of 850° C. This was found to give good results more consistently. The first poke to break the crust during reduction was eliminated, as it was found to be unnecessary and only added more work and was another possible way of introducing air. A rotating feed arm was installed in the reaction vessel to distribute the titanium tetrachloride over a larger area and, thus, prevent local overheating. The process, conducted in a batchwise manner as described and followed by good purification and fusion, produces a metal adequate in quality for nearly all purposes.