RI 5850 Zirconium-Gadolinium Equilibrium Diagram ? Summary

The investigation of the zirconium-gadolinium equilibrium diagram was part of a program to investigate rare:earth alloys for use as nuclear reactor control materials. Investigation of the zirconium-gadolinium equilibrium diagram revealed a eutectic system with limited terminal solubilities and one peritectoid reaction. The eutectic composition occurs at about 82 percent gadolinium, and the eutectic isotherm, which occurs at 1,220 ±5° C., extends from about 12 to 99+ percent gadolinium. A peritectoid isotherm occurs at 890 ±5° C. and extends from about 2 to 99+ percent gadolinium. The solubility of gadolinium in beta zirconium decreases from about 12 percent at 1,220 ±5° C. to about 2 percent at 890 ±5° C. The solubility of gadolinium in alpha zirconium decreases from approximately 5 percent at 890 ±5° C. to between 2 and 3 percent at 600° C. Vary little solubility of zirconium in gadolinium was indicated. An allotropic transformation of gadolinium was observed at 1,260 ±5° C. A change of the gadolinium transformation temperature on alloying with zirconium was not observed.