RI 5878 Determination Of Oxide Solubility In Molten Fluorides ? Summary

The solubility of UO2 was determined at 1,250° C. in ternary melts of UF4 and BaF2 with CaF2, LiF, and SrF2. The solubility of Ce02 was measured at 800° and 850° C. in a solution of CeF3, BaF2, and LiF. The amount of La203 which dissolves at 950° C. in a binary mixture of LiF and LaF3 and a ternary of LiF, LaF3, and BaF2 was also measured. In each case, the amount of soluble oxide was mound to be less than 5 weight-percent. A procedure was developed for filtering fused, oxide-saturated fluoride melts in order to obtain a representative sample for chemical analysis. The oxide content of the samples was determined by an inert-gas fusion procedure.