RI 6075 Electrowinning Molten Lanthanum From Lanthanum Oxide

High-purity lanthanum metal was prepared by electrolysis of La003 in a LaF3-LiF-BaF2 bath at 950° C. The requisite bath temperature for the deposition of molten metal was maintained by supplying the heat as current directly to the electrodes. A current efficiency of about 60 percent was obtained. The lanthanum nodules contained carbon and oxygen as major impurities. The total impurity content was from about 0.1 to 0.2 percent.