RI 6418 Corrosion Resistance of Diborides in the Psendodibinary System TiB

Tests of resistance to molten metals , to oxidation at elevated temperatures , and to various chemical reagents were made for a series of compositions in the TiB₂ - CrB₂ subsystem . In reaction with molten metals , there was no noticeable difference in reaction of the various compositions in the ( Ti , Cr ) B₂ series . The oxidation tests were ( 1 ) a rising - temperature test in which the specimen temperature was increased 4° per minute to 1,200 ° C and ( 2 ) a constanttemperature test in which the specimen temperature was held constant at 1,000 ° C. Compositions near Tio.6 Cro.4 B2 had the best oxidation resistance . Ti。.6 The chromium- rich alloys showed marked superiority to the titanium- rich alloys in resistance to corrosion by the chemical agents investigated . The chemical reagents used were sulfuric , nitric , and hydrochloric acids and sodium hydroxide of different concentrations .