RI 7320 The Sysrem Al4C3-AlN-Al203 - Powder Forming And Sintering Behavior, Phase Identification, And Refractory Composition Properties

The ternary system A14C3-AIN-Al203 has been examined to determine compositions which may display desirable high-temperature refractory properties. Powder methods were employed in the synthesis of all test compositions. Forming and sintering behavior was examined and hot-pressing parameters were measured. Several properties were studied for each composition of interest in the system. The properties included hydrolysis rate in moist air, elevated temperature oxidation rate, density, softening point, tensile strength, and rupture strength. In most cases equilibrium was not achieved, and the data are representative of a nonequilibrium system. Approximately 16 separate phases have been observed in the system. Forming behavior and selected properties of five compositions of interest were compared with those of aluminum oxide and aluminum nitride. None of the compositions compared favorably. Oxidation and vaporization appear to be serious drawbacks to the use of these compositions at elevated temperatures.