Secondary Cooling Technology for Casting of Hypo-Peritectic Steels

From the standpoint of quality, surface cracks normally pose more of a problem than internal cracks. Hypo-peritectic (HP) steel grades are well known for their proneness to surface longitudinal cracking (SLC) during continuous casting. This study analyzed the influences of chemical composition, technique parameter and secondary cooling on the surface longitudinal cracks. Based on the optimized the first and secondary cooling zone water distribution in the process of continuous casting, low cooling water distribution at solidification initial stages and uniform cooling at secondary cooling zone were suggested, which can be used to effectively control the surface longitudinal cracks.