Selective flotation of chalcopyrite and molybdenite by surface oxidation

For pretreatment of selective flotation, surface oxidation of chalcopyrite and molybdenite was applied by oxygen plasma then the minerals were washed by solution at pH 9 with oxygen bubbling. Surface characteristics of these minerals were investigated with AFM, XPS, zeta potential and contact angle measurements. Contact angle of chalcopyrite and molybdenite decreased a lot by plasma treatment. When they were washed with pH 9 solution with oxygen bubbling, contact angle of molybdenite increased whereas chalcopyrite one kept low. Adhesion force measurements indicated similar behavior. Result of flotation experiments indicated low recovery of both chalcopyrite and molybdenite after plasma treatment and only molybdenite recovery became higher after washing. Selective flotation of chalcopyrite and molybdenite could be achieved with this process. Possible mechanism of selective flotation was proposed from the results of XPS, AFM, etc.