Single Pass Large Draught Rolling of Magnesium Alloy Sheets by High Speed Rolling

Present authors have succeeded in single pass large draught rolling of AZ31 and ZK60A magnesium alloy sheets below 200 °C without heating rolls by raising rolling speed above 1000 m/min. Heavy reduction larger than 60% can be applied by single pass high speed rolling even at room temperature. The rolled sheets showed fine recrystallized microstructure by dynamic recrystallization. The improvement of workability at lower rolling temperature is due to temperature rise by plastic working. In high speed rolling, almost all of the work done by plastic deformation is converted into the heat that raises the temperature of the sheet during rolling because the heat did not flow out of the sheet by conduction and radiation within very short time.