Slag-metal equilibrium in the production of Iow-carbon ferromanganese

An investigation was conducted into the reactions between the slag system MnO-CaO-MgO-SiO2(AI2O3) and the alloy system Mn-Fe-Si-(C). Synthetic slags representative of plant melts and a plant alloy were reacted in alumina crucibles at temperatures of 1400°C, 1450°C, 1550°C, and 1600°C. In similar experiments, slags were used that comprised a South African manganese ore with various amounts of lime and several synthetic alloys with various silicon contents and manganese-to-iron ratios. These experiments were conducted in a vertical molybdenum-wound resistance furnace with full temperature control. Slag-to-alloy ratios were also varied during the tests. The rate of reduction of Mn.O3 and the MnO from the slag by the silicon in the alloy was extremely rapid, most of the reaction being completed within five minutes. The strongly exothermic nature of the reaction resulted in considerable generation of heat at the slag-alloy interface, causing convectional stirring of the contents of the crucible and promoting the rate of reaction. Equilibrium was usually attained after fifteen minutes. The major limitation governing the recovery of manganese is the need for the silicon content of the alloy to meet a maximum specification of 2 per cent. Higher concentrations of silicon in the final alloy of between 8 and 12 per cent favour good recoveries of manganese from the slag, but, since such an alloy is not salable, lower recoveries must apparently be tolerated. In alloys of 2 per cent silicon, low activities of the silicon are responsible for poor recoveries of manganese. The activity of MnO in the slag can be increased by moderate additions of CaO and small amounts of MgO, i.e., by an increase in the basicity of the slag.