Study of Electroslag Remelting of Cu-Cr-Zr Alloy

The ESR of Cu-Cr-Zr alloy has been experimentally investigated. The remelting experiments have been carried out with different slag fluxes in the Cal, + Nal, CaF2 + ZrO2 and CaF2 + NaF + ZrO2 systems on an ESR furnace of 25kg capacity; using a water-cooled copper mould of 96.5 mm diameter, with the forged square bar electrodes of 50x50 mm2. The slag amount was taken to be 1.5 kg. The remelting current and voltage used were 1600-1800A and !5-25K, respectively. The influence of the slag composition on the stability of the remelting process and the losses of alloying elements (2r and Cr) has been considered and examined. The technologies of hot working and heat treatment of the ES ingot have been described and discussed. Some physical properties of the slag in a CuF2 + NaF + ZrO2 system and the remelted Cu-Cr-Zr alloy have been determined. The results indicated that with the slag flux of CaF2 + NaF + l0 mass % ZrO2 and the other operation parameters employed, a high quality ingot of Cu-Cr-Zr alloy may be obtained at the considerably high yields of Zr and Cr by means of ESR. For the remelted Cu-Cr-Zr alloy with a specified composition of 0.5 mass % Cr and 0.1 mass % Zr, the appropriate electrical conductivity, hardness and softening temperature are as high as 45-46S/m, HRB 82-84 and 550°C. respectively. The properties of the Cu-Cr-Zr alloy products are in accordance with and superior to the requirements and specifications of ISO5l82-l99l(E).