Study on Corrosion Resistance of Electrodeposited RE-Ni-W-P-SiC Composite Coating

"Corrosion resistance of RE-Ni-W-P-SiC composite coating and 3 l6L stainless steel in corrosion media of H2SO4, HCl, H3PO4 and FeC13 solutions at different concentrations by means of immersion methods and anodic polarization curves obtained by DHZ-1 electrochemical synthetic tester and HDV-7 transistor constant potentiometer. Immersion experiment results show that corrosion rate of RE-Ni-W-P-SiC composite coating as-deposited in HCl solutions increases with the rise of HCl concentrations, on the contrary, the corrosion rate of the composite coating after heat treatment decreases with increasing the HCl concentrations the corrosion rates of the coatings as-deposited and after heat treatment in H2SO4 and H3PO4 solutions respectively decrease with the rise.of H2SO4 and H3PO4 concentrations the corrosion rate of the deposit as-deposited in FeC13 solutions decreases with increasing FeC13 concentrations, while the rate of the composite coating after heat treatment increases .with the rise of FeC13 concentrations.In addition, the corrosion rate of 3 l 6L stainless steel in the corrosion media of H2SO4, HCl, H3PO4 and FeC13 solutions at different concentrations increases with rising of concentrations. Furthermore, the corrosion rate of 316L stainless steel in the corrosion media of H2SO4, HCl, H3PO4 and FeC13 solutions respectively is much greater than that of the RE-Ni-W-P-SiC composite coating as-deposited and after heat treatment in the same corrosion media.1. IntroductionAll the materials and their products, when processed, stored and used, it is inevitable that the corrosion, wear, fatigue and crack occur owing to the actions of surroundings. Those early failure and abrasion, through all kinds of departments and profession that corrosion consumes one percent of tens of the steel products of the whole world; and two or four percent of the GDP is lost because of the corrosion."