Study on Solidification/Sintering Brick Making with EMD Residue

"Electrolytic manganese dioxide (EMD) residue was mixed with shale and fly ash as the main materials to make solidification/sintering brick for the utilization of the residue from EMD production. The effects of sintering temperature, sintering time, solid waste content and cooling process on its mechanical properties and toxic elements solidification were investigated according to compressive strength and leaching toxicity. The results showed that the calcined residue had capability of solidifying toxic metals and exhibited perfect strength after treated in the optimal parameters of EMD residue below 50%, temperature at 1000-1100°C, time3-5h, and semi-quenched at 600°C1 InstructionSolid clay-brick holds the leading position among building materials for a very long time in China. The traditional technique of making clay-brick has the drawbacks of backward process, simple facilities and single product. Since Chinese Reform and Opening-up, urban-rural construction and real estate have been booming with the rapidly development of national economy and science technology. The problems of ruining fertile land, environment contamination and high energy consumption in the traditional technique of clay-brick making have not been solved yet. On the other hand, more than 7 billion tons of industrial wastes are accumulated over years which occupies over 6.7 million hectares filed and causes serious environmental problems[1-31. Strategy present in ""The Chinese Agenda of the 21st Century"" required the production of wall materials less energy conservation, land saving and waste recycling.Coal gangue[4-9l, fly ash[I0- 13l, sludge from waste water treatment and tailings of gypsum, pyrite, copper mine, high silicon containing iron, asbestos and ects [l4-lSJ are the solid wastes used for brick making around the world. There are two kinds of process for brick making, high temperature sintering and low temperature steam curing[19•201. Although the technology of two brick making made great progress and got widely application in construction field, no precedent for preparing sintering-bricks with EMD residue as materials occurred in China because of its complicated processing technics and lack of sufficient practical experience to guarantee the bricks' quality.In this study, EMD residue was mixed with shale and fly ash as the main materials to make solidification/sintering brick. The effects of sintering temperature, sintering time, solid waste content and cooling process on its mechanical properties and toxic elements solidification were investigated according to compressive strength and leaching toxicity."