Technical Notes - An Observation on Diffusion during Homogenization of a Single Crystal of Alpha Brass (Metals Tech., Sept. 1948, TN 6)

crystal prior to, polishing in order to eliminate coring. This treatment may be accomplished by wrapping the single crystal tightly in very thin, dead soft, brass foil and annealing in the presence of air for 20 hr at 800°C. Since the wrapping encircles the sptcimen three to four times, only a very slight amount of oxidation occurs on the specimen surface. On unwrapping one of these cylindrical single crystals. in. in diam by ro in. long (72.75 pct cu, 27.23 pct Zn, 0.01 pct P11, 0.01 pct re), mall light-gray depnrrits in the form of circular arcs werenoted on the part nf the foil which had been in contact with the single crystal, Fig r. (By superim- approximatetl). These deposits, which, from their color, suggest the appearance of sublimated zinc, were found to coincide roughly with a set of octahedral planes nearly perpendicular to the rod axis. The pattern shorn in the figure held no relation to the profle of the sample since the markin~s on the crystal More annealing werc attributed to traces of cube planes. It seems very likely that the deposits were formed by sutllimation of zinc diffusing from octahrdral planes since diffusian would Eogically take place along planes of maximum atomic spacing. However, it is difficult to understand why a continuous sublimation of zinc should occur from a single crystat in contact with a wrapping roil OF the same composition, and why diffusion would take place along specific octahedral planes and in a regular pattern.