Technical Notes - Sigma Phases Containing Osmium and Iridium

DURING the course of the present investigation of alloy phases involving transition metals, phases were found in the systems Os-Ta, Os-W, and Ir-Ta. The (Os, W) phase was also recently reported by Raub.1 Pertinent information is given in Table 1. The approximate composition range of sta- bility was determined metallographically on arc-melted buttons that were annealed 72 hr at 1200°C and water quenched. X-ray powder patterns were obtained with a 114.6 mm diam powder camera using filtered copper radiation. The composition for (Os, W) given by Raub (66 atomic pct W) is in agreement with the composition range reported here. However, the lattice constants reported by Raub are: a0= 9.913±0.007, c/a= 0.515. The reason for the discrepancy between the lattice constants reported by Raub and those given here is not known. Acknowledgments The authors wish to thank M. H. Mueller and H. W. Knott for assistance with the X-ray diffraction work, and R. A. Morris for the preparation of the alloys. This paper is based upon work performed at the Argonne National Laboratory under the auspices of the Atomic Energy Commission.