The Manufacture and Characteristics of Wrought-Iron

I. INTRODUCTION. THOSE who deem the subject of this paper an old and super¬seded one may recall with advantage the words of the great proverb-maker, bidding us to seek the new in the ashes of the old. The manufacture of wrought-iron began with the small hearth built upon an eminence, and relying on the wind for blast. Next came, either the hearth about 12 in. in diameter by 2 ft. in height, blown by a man operating two goat-skins for bellows, or, a hearth of greatly varying diameter and about 10 ft. high, depending for its blast upon natural draft. The former appeared in India, the latter in Burmah; and both were in operation until quite recently, though their origin is lost in prehistoric times. The Catalan forge was the evolutionary descendant of the foregoing, and the parent of the Blase-ofen, which in turn led to the high bloomary or " Stückofen," the father of the blast-furnace, as a producer of cast-iron. The production of cast-iron checked the growth of the direct processes; and led to the introduction of various hearths, such as the Walloon, for low-silicon irons; and the South Wales process, combining the run-out fire with the finery, for higher-silicon irons. Some of these are still in operation in localities possessing the necessary raw materials; and their product is used for purposes requiring wrought-iron of exceptional quality, the supply of which is still smaller than the demand. We have to look back but a century and a quarter to see the introduction of the puddling process by Henry Cort; a process which, reinforced by the iron-oxide bottoms and fettling of Hall, was not less revolutionary in character, and more revo-