The Microstructure Of Aluminum

IT is well known that the so-called pure aluminum contains noticeable amounts of impurities, chiefly iron and silicon, and many investigators have studied the forms in which these impurities exist. Hanson and Archbutt1 state that iron exists in aluminum as FeAl3 and silicon as elementary Si. The solubility of FeAl3 in solid aluminum is practically zero, or at, least so small that the smallest trace of this compound is always visible as a separate constituent. Under the microscope an untrained eye can hardly distinguish, without etching, the two constituents FeAl3 and Si, but they can be differentiated by suitable etching reagents. Anderson2 also found the same results. At the same time, Merica, Waltenberg, and Freeman3 found a constituent of unknown composition. They found a small thermal effect, at 610° C., on the cooling curves of aluminum with small amounts of iron and silicon. The intensity of this effect increased with increasing silicon content, until an effect occured at 576° C. due to the eutectic between aluminum and silicon. The authors ascribed the effect at 610° C. to a compound, which they call "X constituent." It was thought to be a ternary compound containing iron and silicon and could be observed under the microscope as dark particles. Dix4 has published unetched photomicrographs of an aluminum with 0.51 per cent. iron, 0.99 per cent. silicon, and 0.32 per cent. copper that shows three constituents: the dark Si (black in the figure), the lighter FeAl3, which appears in half tone and crystallizes in needles, and a constituent of the same color as FeAl3 but of different crystal form, often resembling Chinese script. This last constituent, Dix thought, is a compound of Fe and Si; not the compound FeSi but a compound containing a relatively small amount of silicon. Therefore an alloy of aluminum, iron, and silicon (the copper should not be regarded in the following considerations) must contain the following four constituents: Al, FeAl3,