The Production Of Converter-Matte From Copper-Concentrates By Pot-Roasting And Smelting

THE experiments here described were made under my supervision while temporarily acting as head of the Department of Metallurgy at the Missouri School of Mines, at Rolla. The work was done by Messrs. W. E. Brown, W. C. Richards, and F. L. L. Wilson, and the description of the results forms a portion of a thesis presented for the degree of Bachelor of Science. These results are submitted because I have seen no description of the application of pot roasting to the treatment of a copper-concentrate. This work followed that already described in the discussion of the ' Lime-Roasting of a Galena-Concentrate,"' and was similarly occasioned by the lack of a furnace of the reverberatory type in which the copper-concentrates could be smelted. The material for the tests was a mixture of three lots available. The first consisted of 8-mm. jig-concentrates and the second of 0.5 mm. table-concentrates, from the San Juan district, Colo. Both contained pyrite, chalcopyrite and galena. The third was a lot of copper-ore, found in the laboratory, which had been crushed through 8-mm. screen, and had at some previous time, before the laboratory roasting-furnace was torn down, received a partial roasting. The analyses of these ores are given in Table I. In order to determine the applicability of pot-roasting as to each lot of ore, and the effect of varying proportions of lime, six preliminary tests were made in a " size N " Battersea crucible, 9 in. high by 6 in. in diameter at top, with a 5/8 in. hole bored through the bottom. The crucible was set in the upturned elbow of a 2-in. pipe, the joint being luted with clay; and air was obtained from a receiver supplied by a compressor. The