The Technical Analysis of Lead Blast Furnace Slag, as Practised at the Port Pirie Works of The Broken Hill Associated Smelters Pty. Ltd.

THE slag from the blast furnaces having been granulated, a representative sample is taken to the sample mill. It is then dried, crushed through a 100-mesh screen, intimately mixed, and packeted for assay purposes.METHOD OF ANALYSISINSOLUBLEWeigh 1 grm. of the finely-pulverized slag into a 3t-in. casserole, moisten with a little water to prevent sticking, cover with a clock glass, and add 20 cc. of hot acid (1 HNOs, 3 HCI, 4 H2 0). Evaporate slowly to dryness on a hot plate and bake (without overheating) until all the gelatinous silica is dehydrated. Cool, add 20 cc. HCI (1-1), and boil gently for several minutes; filter into a 300-cc. beaker, cleaning out the casserole thoroughly with a rubber-tipped glass rod. Wash residue with hot distilled water and transfer it to a No. 1 porcelain crucible. Dry, ignite, cool in a desiccator and weigh as total insoluble matter. Dilute filtrate to 200 cc. and neutralize some of the excess HCI with NHa.OH. Warm, and pass H2S for 15 min. Filter and wash withhot water. Boil off H2 S, oxidize with 5 cc. HNOll , reduce bulk of the solution by evaporation. to about 100 cc., and transfer to a 250 cc. flask.SILICAFuse insoluble residue over a blast lamp in a platinum crucible with three or four times its weight of anhydrous carbonate of soda, for 10 to 15 minutes, or until decomposition is complete. Cool, and extract fusion in an 8-in. evaporating dish with HCI (1-1); rinse crucible and cover with distilled water, and evaporate to dryness over a water bath. Take up dry mass with 10 cc. strong HCI, and then.