Thermodynamics of Tungsten Ores Decomposition Process Options

The thermodynamics of tungsten ore decomposition in mineral acid and alkaline solutions were studied. The published thermodynamic data of tungsten minerals were collected and assessed. The Gibbs energies of CaWO4 (−1538.43 kJ/mol), FeWO4 (−1053.91 kJ/mol), MnWO4 (−1206.08 kJ/mol), H2WO4 (−1003.92 kJ/ mol), and Na2WO4 (−1455.58 kJ/mol, aq) at 25 °C were adopted in the calculation using HSC software. The results show that CaWO4 is decomposed more readily in Na2CO3 solution than in NaOH,while FeWO4 andMnWO4 aremore reactive inNaOH solutions. Froma thermodynamic point of view, tungsten ore decomposes easily in acid solutions despite most ΔGo T increasing slightly with temperature. Oxidizing Fe2+ to Fe3+ in acidic solutions facilitates decomposition of FeWO4, and the reaction of CaWO4 in H2SO4 solution occurs more easily than in other mineral acids, due to the formation of sparsely soluble CaSO4. The results fit well with the experimental data and industrial experience previously reported in the literature.